| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 機械性能 | 斷裂伸長率 | 23℃ | ASTM D-638 | 2.6 | % |
| 拉伸模量 | 23℃ | ASTM D-638 | 10000 | MPa | |
| 撓曲模量 | 23℃ | ASTM D-790 | 8965 | MPa | |
| 埃佐缺口沖擊強度(lzod) | 23℃ | ASTM D-256 | 112 | J/m | |
| 埃佐無缺口沖擊強度(lzod) | 23℃ | ASTM D-4812 | 998 | J/m | |
| 撓曲強度 | 23℃ | ASTM D-790 | 200 | MPa | |
| 拉伸強度 | 23℃ | ASTM D-638 | 140 | MPa | |
| 電氣性能 | 表面電阻率 | --- | ASTM D-257 | 0.1E15 | Ohm |
| 耗電因數 | 1E3Hz/1E6Hz | ASTM D-150 | 0.002/0.018 | --- | |
| 介電常數 | 1E3Hz/1E6Hz | ASTM D-150 | 4/3.8 | --- | |
| 介電強度(短時) | 1.6mm/3.2mm | ASTM D-149 | 23/17 | Kv/mm | |
| 體積電阻率 | --- | ASTM D-257 | 1E16 | Ohm-cm | |
| 加工性能 | 干燥時間，除濕式干燥機 | --- | --- | 2-4 | h |
| 干燥溫度 | --- | --- | 110-130 | ℃ | |
| 加工濕度率 | --- | --- | ＜0.04 | % | |
| 熔膠溫度 | --- | --- | 240-260 | ℃ | |
| 模溫 | --- | --- | 30-130 | ℃ | |
| 熱性能 | 熔融點 | --- | ASTM D-3418 | 225 | ℃ |
| 熱變形溫度 | 0.45MPa/1.8MPa | ASTM D-648 | 220/205 | ℃ | |
| 其它性能 | 比重 | --- | ASTM D-792 | 1.53 | --- |
| 收縮率 | 縱向/橫向 | --- | 0.3/1 | % | |
PBT
聚對苯二甲酸丁二醇酯，英文名polybutylene terephthalate（簡稱PBT），屬于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)與對苯二甲酸(PTA)或者對苯二甲酸酯(DMT)聚縮合而成，并經由混煉程序制成的乳白色半透明到不透明、結晶型熱塑性聚酯樹脂。與PET一起統稱為熱塑性聚酯，或飽和聚酯。